Ni-Span C902 Wire

  • Price:

    Negotiable

  • minimum:

  • Total supply:

  • Delivery term:

    The date of payment from buyers deliver within days

  • seat:

    Shanghai

  • Validity to:

    Long-term effective

  • Last update:

    2019-06-17 21:10

  • Browse the number:

    292

Send an inquiries

Company Profile

Huona (Shanghai) New Material Co., Ltd.

By certification [File Integrity]

Contact:huona(Mr.)  

Email:

Telephone:

Phone:

Area:Shanghai

Address:Shanghai

Website:http://www.ni-alloys.com/ http://huona.manbandtools.com/

PRODUCT DETAILS

Ni-Span C902 wire a precipitation hardenable Nickel-Iron-Chromium alloy having outstanding controllable thermoelastic coefficient characteristics and excellent oxidation resistance in high temperature atmospheres. The alloy can be processed to have a constant modulus of elasticity at temperatures ranging from -45 to +65oC (-50 to +150oF).

Chemical composition

Composition

%

Fe

Ni

Cr

Ti

Al

C

Mn

Si

p

S

Content

min

Bal

41.5

5.2

2

0.5






max

43.5

5.8

2.7

0.8

0.0.5

0.8

0.8

0.02

0.02

Typical Physical properties

Density (g/cm3)

8.05

Electrical resistivity at 20ºC(OMmm2/m)

1.0

Melting point ºC

1480

Thermal conductivity, λ/ W/(m*ºC)

12.98

Elastic Modulus, E/ Gpa

176~206

Coefficient of Expansion μm/m °C (20 – 100°C)

7.6

Modulus of Rigidity (kN/mm²)

62-69

Modulus of Elasticity (kN/mm²)

165-200

Key Features

                   

Outstanding controllable thermoelastic coefficient characteristics Can be processed to have constant modulus of elasticity from from -45 to +65ºC (-50 to +150ºF) Good for springs in watches and weighing equipment

Age hardenable

Typical Applications

Springs in precise applications, such as watches and weighing machines